High Temperature Stability: |
Excellent |
Size: |
customized |
Low Thermal Expansion: |
Excellent |
Purity: |
96%,99% |
Dielectric Constant: |
9.8 |
Dielectric Strength: |
15 kV/mm |
Elastic Modulus: |
380 GPa |
Method: |
lsostatic presure |
Max Operating Temperature: |
1700°C |
Color: |
White |
Maximum Use Temperature: |
1700c |
Electrical Resistivity: |
10^14 Ohm-cm |
Melting Point: |
2040°C |
Compressive Strength: |
3000 MPa |
Water Absorption: |
0 |
High Temperature Stability: |
Excellent |
Size: |
customized |
Low Thermal Expansion: |
Excellent |
Purity: |
96%,99% |
Dielectric Constant: |
9.8 |
Dielectric Strength: |
15 kV/mm |
Elastic Modulus: |
380 GPa |
Method: |
lsostatic presure |
Max Operating Temperature: |
1700°C |
Color: |
White |
Maximum Use Temperature: |
1700c |
Electrical Resistivity: |
10^14 Ohm-cm |
Melting Point: |
2040°C |
Compressive Strength: |
3000 MPa |
Water Absorption: |
0 |
Alumina ceramics là vật liệu được sử dụng rộng rãi nhất trong các loại gốm mịn khác nhau, mà sau khi trải qua quá trình ngâm, có cấu trúc tinh thể tương tự ((AlzO3) như sapphire và ruby.Các vật liệu này được sử dụng trong một loạt các lĩnh vực công nghiệp do các đặc tính vật liệu tuyệt vời của chúng như cách điện cao, sức mạnh cơ học cao, và cao mòn và hóa chất-chống.